PAPERS
- ARTIGOS |
Influência do
tipo de tratamento da superfície de resíduos de
borracha de pneus adicionados em argamassas |
Influence
of the surface treatment of tire rubber residues
added in mortars |
|
Full Paper: |
|
|
|
|
A.
C. MARQUES, J. L. AKASAKI, A. P. M. TRIGO, M. L.
MARQUES |
|
Abstract
In this work it
was evaluated the influence tire rubber addition
in mortars in order to replace part of the sand
(12% by volume). It was also intended to verify
if the tire rubber treatment with NaOH saturated
aqueous solution causes interference on the mechanical
properties of the mixture. Compressive strength,
splitting tensile strength, water absorption,
modulus of elasticity, and flow test were made
in specimens of 5cmx10cm and the tests were carried
out to 7, 28, 56, 90, and 180 days. The results
show reduction on mechanical properties values
after addition of tire rubber and decrease of
the workability. It was also observed that the
tire rubber treatment does not cause any alteration
on the results compared to the rubber without
treatment.
Keywords: tire rubber mortar,
mechanical properties, and waste management. |
|
Resumo
Neste trabalho foi avaliada a influência
da adição de borracha de pneus em argamassas substituindo
parte da areia (12% em volume). O trabalho também
tem como objetivo verificar se o tratamento da
superfície da borracha com solução aquosa saturada
de NaOH, causa interferência nas propriedades
mecânicas das misturas. Foram feitos ensaios de
trabalhabilidade, resistência à compressão, resistência
à tração e módulo de elasticidade em corpos-de-prova
de 5x10(cm) para as idades de 7, 28, 56 e 90 dias.
Os resultados mostram redução nos valores das
propriedades mecânicas após a adição da borracha
de pneu e perda da trabalhabilidade. Também foi
observado que o tratamento da superfície da borracha
de pneu não demonstra alteração nos resultados
quando comparados com os resultados dos corpos-de-prova
que não sofreram tratamento.
Palavras-chave: argamassa com
borracha de pneu, propriedades mecânicas e resíduos. |
|
Deformations
in the strut of two pile caps |
Deformações
nas diagonais comprimidas em blocos sobre duas estacas |
|
Full Paper: |
|
Trabalho Completo:
|
|
|
R.
G. DELALIBERA, J. S. GIONGO |
|
Abstract
There are several
models for the design of pile caps, one of them,
is the strut and tie model. Struts are graphical
representations of the flows of the compression
principal stress, while, the tie represents the
flows of the tensile principal stress. The NBR
6118:2003 [1] recommends the use of strut and
tie model for the design and verification of pile
caps. The use of simple strut and tie models is
much used by engineers. Basically, the model consists
in determining steel areas based on the traction
tie and verifying the crushing of the concrete
in the inferior and superior nodal zones (the
interface between the inferior face of the pile
cap and the pile is the inferior nodal zone and,
the interface between the superior face of the
pile cap and the column, is the superior nodal
zone). The strut integrity is guaranteed when
the stress intensities in the superior and inferior
nodal zones are lower than the limit value. This
limit value is determined in function of the mechanical
properties of the concrete pile cap and the stresses
in the strut are determined in function of the
internal forces and the area of the inferior and
superior nodal zones. The correct form of the
diagonal compression inside the pile cap is unknown.
In function of the experimental analysis of the
principal compression strain, the geometric form
of the strut to two pile caps submitted the centered
and eccentric load is shown along with the intensity
of the stress in the inferior nodal zone.
Keywords: Reinforcement concrete,
strut and tie model, experimental analysis, pile
caps. |
|
Resumo
Existem vários modelos para o dimensionamento
de blocos sobre estacas, sendo que um deles é
o modelo de escoras (bielas) e tirantes. Escoras
são representações gráficas dos fluxos das tensões
principais de compressão de um dado elemento,
enquanto que os tirantes representam os fluxos
das tensões principais de tração deste. A NBR
6118:2003 [1] recomenda a utilização de modelos
de escoras e tirantes para o dimensionamento e
verificação de elementos estruturais de volume,
idéia que se aplica aos blocos sobre estacas.
Os conceitos de modelos de escoras e tirantes
são simples e muito utilizados na análise de estruturas
de concreto. Basicamente, o modelo consiste em
determinar às áreas das barras de aço da armadura
principal de tração por meio das tensões de tração
obtidas para o tirante e verificar a ruptura do
concreto da diagonal comprimida junto à zona nodal
inferior e superior (entende-se por zona nodal
superior e inferior as interfaces pilar-bloco
e estaca-bloco respectivamente). A integridade
da diagonal comprimida é garantida quando as intensidades
das tensões nas zonas nodais superior e inferior
são menores que um valor último. Esse valor último
é determinado em função das propriedades mecânicas
do concreto do bloco e as tensões nas zonas nodais
inferior e superior são determinadas em função
da força resultante das tensões atuantes na diagonal
comprimida e de suas áreas. A forma correta da
diagonal comprimida no interior do bloco é desconhecida.
Por meio de uma análise experimental obtiveram-se
as deformações principais de compressão e a forma
geométrica das diagonais comprimidas em blocos
sobre duas estacas submetidos à ação de forças
centrada e excêntrica, como também as intensidades
das tensões atuantes na zona nodal inferior.
Palavras-chave: Concreto armado,
modelo de escoras e tirante; análise experimental;
blocos sobre estacas. |
|
Axial compression
behavior of concrete masonry wallettes strengthened
with cement mortar overlays |
Axial
compression behavior of concrete masonry wallettes
strengthened with cement mortar overlays |
|
Full Paper: |
|
|
|
|
F.
L. DE OLIVEIRA, J. B. DE HANAI |
|
Abstract
This paper presents
the results of a series of axial compression tests
on concrete block wallettes coated with cement
mortar overlays. Different types of mortars and
combinations with steel welded meshes and fibers
were tested. The experimental results were discussed
based on different theoretical approaches: analytical
and Finite Element Method models. The main conclusions
are: a) the application of mortar overlays increases
the wall strength, but not in a uniform manner;
b) the strengthening efficiency of wallettes loaded
in axial compression is not proportional to the
overlay mortar strength because it can be affected
by the failure mechanisms of the wall; c) steel
mesh reinforced overlays in combination with high
strength mortar show better efficiency, because
the steel mesh mitigates the damage effects in
the block wall and in the overlays themselves;
d) simplified theoretical methods of analysis
as described in this paper can give satisfactory
predictions of masonry wall behavior up to a certain
level.
Keywords: masonry wall, concrete
block, cement mortar overlay, composite behavior,
strengthening |
|
Resumo
Este artigo apresenta os resultados
de uma série de ensaios de compressão axial sobre
pequenas paredes de blocos vazados de concreto,
as quais foram revestidas com argamassa de cimento
e areia. Diferentes tipos de argamassa e combinações
com telas de aço soldadas e fibras curtas foram
testados. Os resultados experimentais são discutidos
com base em duas abordagens teóricas: por expressões
analíticas e modelo simples de análise pelo Método
dos Elementos Finitos. As principais conclusões
são: a) a aplicação de revestimentos de argamassa
aumenta a resistência da parede, porém nem sempre
do mesmo modo; b) a eficiência do reforço das
paredes sujeitas à compressão axial não é proporcional
à resistência da argamassa do revestimento, porque
ela é influenciada pelo mecanismo de ruína da
parede; c) a combinação de argamassa de maior
resistência com telas de aço soldadas mostrou
melhor eficiência no reforço, porque as telas
de aço controlam melhor o processo de danificação
da parede e do próprio revestimento; d) métodos
simplificados de
Palavras-chave: alvenaria estrutural,
bloco de concreto, revestimento de argamassa,
estrutura mista, reforço. |
|
Influence of
the type of recycled aggregate from construction
and demolition waste on the module of deformation
of recycled aggregate concrete |
Determinação
da influência do tipo de agregado reciclado de resíduo
de construção e demolição sobre o módulo de deformação
de concretos produzidos com agregados reciclados |
|
Full Paper: |
|
Trabalho Completo:
|
|
|
A.
E. B. CABRAL, V. SCHALCH, D. C. C. DAL MOLIN, J.
L. D. RIBEIRO |
|
Abstract
To contribute
to the recycled aggregate concrete study, an experimental
test was made by substituting the natural aggregates
for recycled aggregates of concrete, of mortar
and of red ceramic, which are the three main ingredients
of Brazilian construction and demolition waste.
Besides the aggregate types, the water/cement
ratio (w/c) was also changed from 0.4 to 0.8,
fixing the amount of pre soaking water of the
recycled aggregates. The concrete’s module of
deformation was determined at 28-days age, using
the Brazilian Standard ABNT NBR 8522/03, in cylindrical
specimens. The results show that substituting
the natural aggregates for the recycled aggregates
reduces the module of deformation, and that the
coarse red ceramic recycled aggregate and the
fine concrete recycled aggregate were the ones
that exerted the greatest and the smallest influence,
respectively, on the concrete’s module of deformation.
Keywords: recycling, construction
and demolition waste, concrete, module of deformation.. |
|
Resumo
Com o intuito de contribuir no
estudo de concretos produzidos com agregados reciclados,
produziu-se um traço de referência (com agregados
naturais) e outros 49 traços, substituindo-se
os agregados naturais por agregados reciclados
de concreto, de argamassa e de cerâmica vermelha,
que são os 3 maiores constituintes dos resíduos
de construção e demolição das cidades brasileiras.
Além do tipo de agregado, também variou-se a relação
água/cimento (a/c), entre os valores de 0,4 a
0,8, fixando-se o teor de água na pré-umidificação
dos agregados reciclados. O módulo de deformação
dos concretos foram determinados aos 28 dias,
utilizando-se a norma brasileira ABNT NBR 8522/03,
em corpos-de-prova cilíndricos. Os resultados
apontam que a substituição do agregado natural
pelo reciclado resulta em uma redução do módulo
de deformação, sendo que o agregado graúdo de
cerâmica vermelha e o agregado miúdo reciclado
de concreto foram os que exerceram a maior e a
menor influência, respectivamente, sobre o módulo
de deformação dos concretos produzidos.
Palavras-chave: reciclagem,
resíduo de construção e demolição,
concreto, módulo de deformação. |
|
Bending moments
in beams of reinforced concrete buildings |
Momentos
fletores em vigas de edifícios de concreto armado |
|
Full Paper: |
|
Trabalho
Completo |
|
|
F.
A. N. SILVA, B. HOROWITZ |
|
Abstract
Residential buildings
with slab systems supported by reinforced concrete
beams are widely used in building industry. For
design purposes, the computation of the loads
on supporting beams is performed using simplified
procedures, in which the slab is analyzed as an
isolated element. New Brazilian code keeps the
same recommendation presented in the old code
allowing that, in the case of rectangular slabs
with uniform load, the reactions on supporting
beams may be computed assuming that those reactions
correspond to the loads acting on triangles or
trapezoids determined from the yield lines of
the slab. In a simplified way, it is still allowed
that these reactions may be considered as uniformly
distributed on the slabs supports. The work shows
through illustrative
Keywords: reinforced concrete
beams, bending moments, reinforced concrete slabs. |
|
Resumo
Edifícios residenciais compostos
de sistema de lajes maciças apoiadas em vigas
de concreto armado são largamente utilizados na
indústria da construção civil. Na prática, o cálculo
das reações destas lajes sobre as vigas é feito
através de processos simplificados, nos quais
os painéis de laje são analisados de forma isolada.
A NBR 6118 [1] mantém em seu texto o mesmo teor
da antiga NB-1 [2] permitindo que, no caso de
lajes maciças retangulares com carga uniforme,
as reações possam ser calculadas admitindo-se
que elas correspondem às cargas atuantes nos triângulos
ou trapézios determinados através do método das
charneiras plásticas. De maneira aproximada, a
norma brasileira permite ainda que estas reações
possam ser consideradas como uniformemente distribuídas
sobre as vigas de apoio. O trabalho demonstra
através de exemplos práticos que tal recomendação
pode conduzir a resultados contrários à segurança
e propõe uma correção para o cálculo das reações
de apoio em lajes maciças sobre as vigas de concreto
armado.
Palabras-Clave: vigas de concreto
armado, momentos fletores, lajes maçicas
de concreto armado. |
|